GYPSUM PLASTER

PERONAT

This is the bagged plaster based ready plaster, which may be applied directly on the materials such as brick, concrete, exposed concrete, aerated concrete, pumice concrete, etc. This removes the discrimination between scratch coat and finishing coat.

Physical Form White powder
Plaster/Water Rate 10 kg to 6-6,5 Liters of water
Usage Period 60-90 minutes
Freezing Period 150 minutes
Consumption amount 8,5-9,0 Kg/m³ (at each 1 cm)
Compression strenght 2,5 N/mm² (7 days later)
Flexural Strength 1,5 N/mm² (7 days later)
Dry unit weight 650-750 Kg/m³
Reaction to fire A1 (according to TS EN 13279 – 1)
Standard 13279-1,2 (TYPE B4)

The Surface and the Setting to be Applied

-It should be free of dirty material such as dust, oil and paint.
- The surfaces such as extremely dry, hot and highly absorbent should be moisturized with water.
- The surface of the ceilings should be roughened before applying the plaster or undercoated with a material to ensure attachment of the mortar.
- It should be paid attention that there is no air current and air circulation at the atmosphere during application.
- The application temperature should be between +5 and +35 ˚C.

Application

6-6,5 liters of water is poured down into the mixture bowl; 10 kilograms of Peronat Plaster is added sprinkling into the water. It is awaited for a period of approximately 2-3 minutes in order to cause the plaster to absorb the water. It is mixed with a hand mixer or with the help of a trowel in order to obtain a homogenous mixture. The application thickness is determined with the help of an annular according to the smoothness of the surface. The prepared mortar is applied on the surface with the help of a steel trowel. The mortar is flatted trough surface finishing. The surface is flatted after surface finishing with the help of a steel trowel. If an application of two layers is to be applied, 2nd layer of application should not be started before the 1st layer settles.

Packaging

Polypropylene bags of 25 kg ( ± 2 %)

Storage

At most 15 bags should be stockpiled one on another at a dry place; the bags must not be in contact with the floor and they must be stored protected from humidity and condensation. They must be used within 9 months after production date.

MAKONAT

This is the bagged plaster based ready machine applied plaster, which may be applied directly on the materials such as brick, concrete, exposed concrete, aerated concrete, pumice concrete, etc.

Physical Form White powder
Plaster/Water Rate 10 kg to 5.5-6 liters of water
Usage Period 130-180 minutes
Freezing Period 250-300 minutes
Consumption amount 9.0-9,5 Kg/m³(at each 1 cm thickness)
Compression strength 2,5 N/mm² (4x4x16 blocks)
Flexural strength 1,0 N/mm² (4x4x16 blocks)
Dry unit weight 730-800 Kg/m³
Reaction to fire A1 (According to TS EN 13279 – 1)
Standard 13279-1,2 ( Type B4, applied with spraying)

The Surface and the Setting to be Applied

-It should be free of dirty material such as dust, oil and paint.
-The surfaces such as extremely dry, hot and highly absorbent should be moisturized with water.
-The surface of the ceilings should be roughened before applying the plaster or undercoated with a material to ensure attachment of the mortar.
-It should be paid attention that there is no air current and air circulation at the atmosphere during application.
-The application temperature should be between +5 and +40 ˚C.

Application

Appropriate amount of plaster is prepared (5,5-6 liters of water / 10 kg makonat)in the plastering machine. The application thickness is determined with the help of an annular according to the smoothness of the surface. The mortar is flatted through surface finishing. When the surface starts hardening, it is flatted with the help of a steel trowel. When a light pressure is applied on the surface, if it does not subside, trifilling process can be started. After trifilling process, polishing is made again with a steel trowel and the surface is made ready for painting.

Packaging

Polypropylene bags of 35 kg ( ± 2 %)

Storage

At most 15 bags should be stockpiled one on another at a dry place; the bags must not be in contact with the floor and they must be stored protected from humidity and condensation. They must be used within 9 months after production date.

SATONAT

This has a high adhesion characteristics and it is the last layer of polishing plaster under the paint. It may be applied both on the mortar and the plaster surfaces plastered with satin as well as on the gypsum plasterboards.

Physical Form White powder
Plaster/Water Rate 10 kg to 7 liters of water
Usage Period 120-160 minutes
Freezing Period 300-350 minutes
Consumption Amount 0.2 – 0.4 Kg/m³ (at each 1 cm thickness)
Compression strength 3,0 N/mm² (4x4x16 blocks)
Flexural Strength 1,5 N/mm² (7 days later)
Kuru Birim Ağırlığı 680-720 Kg/m³
Reaction to fire A1 (According to TS EN 13279-1)
Standard TSE EN 13279-1,2 ( Type C6, thin applicable plaster)

The Surface and the Setting to be Applied

-It should be free of dirty material such as dust, oil and paint.
-The surfaces such as extremely dry, hot and highly absorbent should be moisturized with water.
-The surface of the ceilings should be roughened before applying the plaster or undercoated with a material to ensure attachment of the mortar.
-It should be paid attention that there is no air current and air circulation at the atmosphere during application.
-The application temperature should be between +5 and +40 ˚C.

Application

6,5 – 7 liters of water is poured down into the mixture bowl; Satonat Plaster is added sprinkling into the water. It is awaited for a period of approximately 2-3 minutes in order to cause the plaster to absorb the water. It is mixed with a hand mixer or with the help of a trowel in order to obtain a homogenous mixture. The prepared mortar is applied on the surface with the help of a steel trowel.

Packaging

Polypropylene bags of 30 kg ( ± 2 %)

Storage

At most 20 bags should be stockpiled one on another at a dry place; the bags must not be in contact with the floor and they must be stored protected from humidity and condensation. They must be used within 9 months after production date.

KARONAT

Plaster board is the building plaster used in the construction off decorative material such as core, niche and sculptures. KARONAT may be used both for plaster board casting and in affixing the plaster board.

Physical Form White Powder
Plaster/Water Rate 100 gr. plaster / 70 gr. waterUsage
Period 7-12 minutes
Freezing Period 20-30 minutes
Compression strength 8 N/mm² (7 days later)
Flexural Strength 1,0 N/mm² (7 days later)
Specific Bulk Density 650-700 gr/lt
Grain size Over 50 μ % 16-18 *160 μ over % 0-1,0 PH: 7-8
Surface hardness 60 shore D
Standard TSE EN 13279-1,2 (Tip C1, reinforced with fiber, construction plaster for plaster elements)

The Surface and the Setting to be Applied

-It should be free of dirty material such as dust, oil and paint.
-The surfaces such as extremely dry, hot and highly absorbent should be moisturized with water.
-The surface of the ceilings should be roughened before applying the plaster or undercoated with a material to ensure attachment of the mortar.
-It should be paid attention that there is no air current and air circulation at the atmosphere during application.
-The application temperature should be between +5 and +40 ˚C.

Application

6,5-7 liters of water is poured down into the mixture bowl; Karanot Moulding Plaster is added sprinkling into the water. It is awaited for a period of approximately 2-3 minutes in order to cause the plaster to absorb the water. It is mixed with a hand mixer or with the help of a trowel in order to obtain a homogenous mixture. The prepared mortar is poured into the formwork prepared and lubed before. After pouring a layer, a layer of fiber or hemp is laid on that layer of plaster in order to make the mould more flexible and strong. Another layer of plaster is poured down of the laid fiber or hemp. The plaster poured down into the mold will start to warm after a while. The plaster first warmed and then cooled will let itself go after a while. The plaster taken out of the mould is left at the room temperature to dry before mounting.

Packaging

Polypropylene bags of 30 kg ( ± 2 %)

Storage

At most 20 bags should be stockpiled one on another at a dry place; the bags must not be in contact with the floor and they must be stored protected from humidity and condensation. They must be used within 9 months after production date.

YAPONAT

It is used for internal thermal isolation applications with adhesion of EPS, XPS, composite plate or rock wool to gypsum plates and during adhesion of gypsum plates to internal space surfaces, such as concrete, bricks, bims block and gross concrete.

Physical Form White powder
Plaster/Water Rate 10 kg to 5.5 liters of water
Usage Period 60-90 minutes
Freezing Period 140-180 minutes
Consumption amount 5 Kg/m² (at each 1 cm thickness)
Compression strength 6,0 N/mm² (4x4x16 blocks)
Flexural Strength 1,0 N/mm² (4x4x16 blocks)
Dry unit weight 680-720 Kg/m³
Reaction to fire A1 (TS EN 13279-1)
Standard TSE EN 14496

The Surface and the Setting to be Applied

-It should be free of dirty material such as dust, oil and paint.
-The surfaces such as extremely dry, hot and highly absorbent should be moisturized with water.
-The surface of the ceilings should be roughened before applying the plaster or undercoated with a material to ensure attachment of the mortar.
-It should be paid attention that there is no air current and air circulation at the atmosphere during application.
-The application temperature should be between +5 and +40 ˚C.

Application

5 – 5,5 liters of water is poured down into the mixture bowl; 10 kilograms of Yaponat Plaster is added sprinkling into the water. It is awaited for a period of approximately 2-3 minutes in order to cause the plaster to absorb the water. It is mixed with a hand mixer or with the help of a trowel in order to obtain a homogenous mixture. The prepared mortar should be applied to the surface enough intervals in short bursts driven. The bonding process, after the pasted the smoothness of the surface should be checked.

Packaging

Polypropylene bags of 30 kg ( ± 2 %)

Storage

At most 20 bags should be stockpiled one on another at a dry place; the bags must not be in contact with the floor and they must be stored protected from humidity and condensation. They must be used within 9 months after production date.

DERZONAT

It is employed on internal spaces for plasterboard, curtain, light band, molding and decorative aimed applications.

Physical Form White powder
Plaster/Water Rate 10 kg to 5.5-6 liters of water
Usage Period 80-100 minutes
Freezing Period 160-200 minutes
Consumption amount 0.2 – 0.4 Kg/m³ (at each 1 cm thickness)
Compression strength 4,0 N/mm² (4x4x16 blocks)
Flexural Strength 1,0 N/mm² (4x4x16 blocks)
Dry unit weight 680-720 Kg/m³
Reaction to fire A1 (According to TS EN 13279 – 1)
Standard TSE EN 13963

The Surface and the Setting to be Applied

-It should be free of dirty material such as dust, oil and paint.
-The surfaces such as extremely dry, hot and highly absorbent should be moisturized with water.
-The surface of the ceilings should be roughened before applying the plaster or undercoated with a material to ensure attachment of the mortar.
-It should be paid attention that there is no air current and air circulation at the atmosphere during application.
-The application temperature should be between +5 and +40 ˚C.

Application

5,5-6 liters of clean water is poured down into the mixture bowl; 10 kg of DERZONAT is added sprinkling into the water. It is awaited for a period of approximately 2-3 minutes in order to cause the plaster to absorb the water. It is mixed with a hand mixer or with the help of a trowel in order to obtain a homogenous mixture. The application thickness is determined with the help of an annular according to the smoothness of the surface. The prepared mortar is applied on the surface with the help of a steel trowel. If self-adhesive seam band is to be used, the first layer of application is made after affixing the band. If the self adhesive band is not to be used, the first layer of DERZONAT is applied in such a way to fill the joints of the seam and seam band is affixed, and then the second layer of application is made. After DERZONAT is dried, correction is made if necessary.

Packaging

Polypropylene bags of 30 kg ( ± 2 %)

Storage

At most 20 bags should be stockpiled one on another at a dry place; the bags must not be in contact with the floor and they must be stored protected from humidity and condensation. They must be used within 9 months after production date.